Factors such as [10. For honeycomb activated carbon, the wall thickness is a very important parameter, by changing the wall thickness to improve its adsorption efficiency. Under the same porosity, thickness increases, the honeycomb carbon content per unit volume also will increase, which can improve the adsorption capacity. This is because the wall thickness increases, the fluid channel in the cellular cross-sectional area reduced, so the real surface or volume flow rate will increase. At the same time, the contact between adsorbate and carbon efficiency will, there is a balance between the two. Under the given conditions, the balance will determine adsorption increase or decrease. If the adsorbate at higher the diffusion rate diffuses to the inside of the honeycomb wall, and the empty adsorption site can be continuously adsorbed, so the thick-walled honeycomb should have better adsorption efficiency and adsorption capacity"Determination of air velocity and cross-sectional area of empty towerThe empty tower gas velocity is the velocity of gas passing through the entire cross section of the adsorber.The selection of air velocity not only directly determines the size and pressure drop of the adsorber, but also affects the adsorption efficiency.
⑴ Zinc chip ratio. Zinc chip ratio refers to the weight ratio of anhydrous zinc chloride to absolute raw wood chips. Zinc chip ratio has a decisive influence on the pore structure and adsorption properties of activated carbon. The pore structure of activated carbon is often adjusted by zinc chip ratio, which is the most important factor for the production of activated carbon by zinc chloride method.
⑵ The influence of raw material types. As a result of different species, wood resin content and hardness and other properties are different, thus the chemical penetration ability of wood chips have differences. Fir chips are usually the best, pine chips the next, and hard and miscellaneous chips the worst.activated charcoal wholesale australia
⑶ The moisture content of raw materials. The moisture content of the sawdust affects the rate of chemical penetration into the sawdust particles, thus affecting the impregnation time. When the moisture content of sawdust is more than 30%, the impregnation time is more than 8h. Generally, the moisture content of sawdust should not exceed 5%. According to the different production technology, the moisture content of sawdust has different specific indexes.
(4) the influence of wood particle size. When the particle size of wood chips in the production of powdered activated carbon is 6~40 mesh, the particle size of wood chips has no obvious effect on the product quality. The effect of sawdust particle size on product quality is related to the zinc chip ratio used. When the zinc chips are relatively small (such as 80%), the wear resistance and relative density of activated carbon decrease with the increase of sawdust size. When the size of zinc chip is large (e.g. 200%), the wood chip particle size is 0.25~2.0mm, and the wear resistance and relative density of activated carbon are not significantly affected