In domestic has been eliminated. Specific surface area test unified the multi-point BET method at home and abroad, specific surface area measurement standards are developed at home and abroad is based on BET test method, please see our national standard (GB/T 19587-2004) - gas adsorption BET principle of solid material specific surface area measurement methods. Specific surface area testing is actually the more time-consuming jobs, as the adsorption capacity of sample is different, some sample testing may need to spend the whole dayTime, if the test process is not fully automated, the tester can not leave at any time, and should be highly focused, observe the dashboard, control the knob, a little careless will lead to the failure of the test process, which will waste a lot of valuable time of the tester.https://www.dxdcarbon.com/
F - Sorb 2400 specific surface tester is really able to BET method detection instruments (both direct comparison method), the more important F - Sorb 2400 specific surface tester is by far the only specific surface area of the fully automated intelligent testing equipment, the test results with the international high consistency, the stability is very good also, at the same time reduce the human error, improve accuracy test results.Acid-base modification is to use acid, alkali and other substances to treat activated carbon, according to the actual need to adjust the surface functional groups of activated carbon, make it change, improve its ability of adsorption of metal ions, so as to achieve the desired adsorption effect.Acid-base modification of activated carbon is usually carried out to improve the adsorption effect of activated carbon on metal ions represented by copper ions. The commonly used modifiers include HC1, NaOH and citrate 3.It was found that by acid-base modification of common coal activated carbon, the ash content of the activated carbon could be greatly reduced and the specific surface area of the activated carbon could be increasedIf the gas speed is very small, the size of the adsorber is large and uneconomical.
If the gas velocity is too large, the pressure drop will increase and the adsorption efficiency will be affected.The optimum gas velocity was determined by experiment.wood based activated carbon manufacturer
The adsorption design can not pursue too high adsorption efficiency, the empty tower speed value is reduced, it will make the adsorption bed volume, the amount of adsorbent and equipment cost increased greatly;On the contrary, it is not appropriate to take too large empty tower gas speed. Although the equipment cost is low, the adsorption efficiency drops a lot, and the pressure drop of the system will rise rapidly with the increase of the empty tower speed, resulting in excessive power consumption. Therefore, due to the selection of the appropriate air speed of the empty tower, the most suitable air speed of the empty tower is 0.8~1.2m/s"21, according to the empirical conclusion, this design determines
conditions:Treatment air volume :Q=20000 m'h, design temperature is 35° C, pressure is 1.01325×103Pa  Since the proportion of air in exhaust gas is far greater than that of pollutants, the properties of exhaust gas can be approximately viewed as the thermophysical properties of dry air. Please refer to Appendix 9 of Principles of Chemistry to obtain the following data:Properties of air mixture:Fluid density P;=1.147kg/ m', viscosity u,= 1.94×10-5 Pa.S, specific heat capacity C,=1.005kJ/(kg."C)